Laser Resins

Laser Resins

 
 

MODELING
200
GRAY
 

MODELING
BLACK V2
 

MODELING
CLEAR
 

MODELING
GRAY
 

MODELING
WHITE
 

MODELING
TAN
Group
Tensile(MPa) 57-59 47-52 53-63 50-55 46-53 40-44
Elongation(%) 3-7 2-6 1-4 2-4 1-3 2-6
Impact(J/m) 43-44 16-22 17-29 15-17 23-27 15-17
Hardness(Shore) 86-88D 86-88D 85-88D 85-87D 85-90D 84-86D
Flexure Strength(MPa) 92-104 82-86 89-105 89-95 90-105 79-83
Flexure Modulus(MPa) 1700-2000 2050-2150 1600-2000 2250-2470 1550-1750 1970-2190
HDT(°F/°C) 138.02/58.9 135.86/57.7 170.60/77.0 135/57 170.78/77.1 131/55
Viscosity(cP) 675-825 1000-1200 1100-1300 1000-1300 900-1050 1000-1200
Compression Set(%) - - - - - -

 


 

 
 
HEAT
CHAMPAGNE
 
EXPERT
BLACK
 
EXPERT
GRAY
 
EXPERT
TAN
 
ROBUST
CHAMPAGNE
 
SPRING
BLACK
 
SPRING
PINK
Group
Post-curing FormCure at
60℃/60min
FormCure at
60℃/60min + oven 160℃/90min
- FormCure 60°C, 60min FormCure 60°C, 60min - - -
Tensile(MPa) 65 - 80 65 - 85 70-80 62-68 60-68 45-55 1.2-1.3 1.1-1.2
Elongation(%) 1-3 1-2 1-3 3-7 2-4 10-21 45-55 40-55
Impact (J/m) 16 - 27 23 - 39 35-40 27-33 19-22 60-65 - -
Hardness (Shore) 86-88 D 86-88 D 88-90 D 91-93 D 89-91 D 83-86 D 57-60 A 56-59 A
Flexure strength (MPa) 140-160 150-180 115-150 114-118 124-128 65-90 - -
Flexure modulus (MPa) 2550-2750 2950-3100 2050-2500 1980-2050 2090-2130 1000-1500 - -
HDT (℉/℃) 213.8/101 370.4/188 * 154.04/67.8 161.8/72.1 166.8/74.9 125.78/52.1 - -
Viscosity (cP) 550-650 1050-1200 550-660 550-650 1300-1500 500-600 480-550
  * FormCure at 80℃/120min + oven 160℃/180min            
Compression Set(%) - - - - - - 1.5-2.5 1.5-2.5
Layer thickness(um) - - - 0.1 mm 0.1 mm - - -

 

3D Printing Material Groups

Design Concept

Visual Aid for discussion & evaluation

Read more

Prototype Engineering

Simulates ABS,
PE, Rubber ......

Read more

Functional Engineering

Products that outperforms conventional manufacturing

Coming Soon

Specialty

Specific workflow, Specific application, …

Coming Soon

Material Properties Table

For Laser Printer Resins

 
 

MODELING
200
GRAY
 

MODELING
BLACK V2
 

MODELING
CLEAR
 

MODELING
GRAY
 

MODELING
WHITE
 

MODELING
TAN
Group
Tensile(MPa) 57-59 47-52 53-63 50-55 46-53 40-44
Elongation(%) 3-7 2-6 1-4 2-4 1-3 2-6
Impact(J/m) 43-44 16-22 17-29 15-17 23-27 15-17
Hardness(Shore) 86-88D 86-88D 85-88D 85-87D 85-90D 84-86D
Flexure Strength(MPa) 92-104 82-86 89-105 89-95 90-105 79-83
Flexure Modulus(MPa) 1700-2000 2050-2150 1600-2000 2250-2470 1550-1750 1970-2190
HDT(°F/°C) 138.02/58.9 135.86/57.7 170.60/77.0 135/57 170.78/77.1 131/55
Viscosity(cP) 675-825 1000-1200 1100-1300 1000-1300 900-1050 1000-1200
Compression Set(%) - - - - - -

 


 

 
 
HEAT
CHAMPAGNE
 
EXPERT
BLACK
 
EXPERT
GRAY
 
EXPERT
TAN
 
ROBUST
CHAMPAGNE
 
SPRING
BLACK
 
SPRING
PINK
Group
Post-curing FormCure at
60℃/60min
FormCure at
60℃/60min + oven 160℃/90min
- FormCure 60°C, 60min FormCure 60°C, 60min - - -
Tensile(MPa) 65 - 80 65 - 85 70-80 62-68 60-68 45-55 1.2-1.3 1.1-1.2
Elongation(%) 1-3 1-2 1-3 3-7 2-4 10-21 45-55 40-55
Impact (J/m) 16 - 27 23 - 39 35-40 27-33 19-22 60-65 - -
Hardness (Shore) 86-88 D 86-88 D 88-90 D 91-93 D 89-91 D 83-86 D 57-60 A 56-59 A
Flexure strength (MPa) 140-160 150-180 115-150 114-118 124-128 65-90 - -
Flexure modulus (MPa) 2550-2750 2950-3100 2050-2500 1980-2050 2090-2130 1000-1500 - -
HDT (℉/℃) 213.8/101 370.4/188 * 154.04/67.8 161.8/72.1 166.8/74.9 125.78/52.1 - -
Viscosity (cP) 550-650 1050-1200 550-660 550-650 1300-1500 500-600 480-550
  * FormCure at 80℃/120min + oven 160℃/180min            
Compression Set(%) - - - - - - 1.5-2.5 1.5-2.5
Layer thickness(um) - - - 0.1 mm 0.1 mm - - -

 


Item Price Includes Free Shipping to the 48 Continental U.S. States, All resins tested extensively on FormLabs’ printers

×
×